Vibrating-sample magnetometer: Difference between revisions
m v2.04 - Fix errors for CW project (Heading ends with a colon - Reference before punctuation - Heading start with three "=" and later with level two - Spelling and typography) |
Citation bot (talk | contribs) Add: bibcode, pmid, authors 1-1. Removed parameters. Some additions/deletions were parameter name changes. | Use this bot. Report bugs. | Suggested by BrownHairedGirl | #UCB_webform 1723/3610 |
||
Line 1: | Line 1: | ||
[[Image:VSM en.svg|thumb|VSM schematic]] |
[[Image:VSM en.svg|thumb|VSM schematic]] |
||
[[Image:VSM.jpg|thumb|VSM setup]] |
[[Image:VSM.jpg|thumb|VSM setup]] |
||
A '''vibrating-sample magnetometer''' (VSM) (also referred to as a Foner magnetometer) is a scientific instrument that measures magnetic properties based on Faraday’s Law of Induction. Simon Foner at [[MIT Lincoln Laboratory]] invented VSM in 1955 and reported it in 1959.<ref>{{cite journal|last=Foner|first=Simon|year=1959|title=Versatile and Sensitive Vibrating-Sample Magnetometer|journal=Rev. Sci. Instrum.|volume=30|issue=7|pages=548–557|bibcode=1959RScI...30..548F|doi=10.1063/1.1716679}}</ref> Also it was mentioned by G.W. Van Oosterhout<ref>{{Cite journal|last=Van Oosterhout|first=G.W.|date=1956|journal=Appl. Sci. Res.|volume=B6|pages=101}}</ref> and by P.J Flanders in 1956.<ref>{{Cite journal|last=Flanders|first=P.J.|date=1956|journal=IEEE Special Publication, Conference on Magnetism and Magnetic Materials|volume=T-91|pages=315–317}}</ref> A sample is first placed in a constant magnetic field and if the sample is magnetic it will align its magnetization with the external field. The [[Magnetic moment|magnetic dipole moment]] of the sample creates a magnetic field that changes as a function of time as the sample is moved up and down. This is typically done through the use of a [[piezoelectric]] material. The alternating magnetic field induces an electric field in the pickup coils of the VSM.<ref name=":0">{{Cite web|last=SWT Physics Department|title=Vibrating Sample Magnetometer|url=https://gato-docs.its.txstate.edu/jcr:7543b8ec-f619-49c3-888f-01c3ad13c7da/vsm.pdf|url-status=live}}</ref> The current is proportional to the magnetization of the sample - the greater the induced current, the greater the magnetization. As a result, typically a [[Hysteresis|hysteresis curve]] will be recorded<ref name=":1">{{Cite journal| |
A '''vibrating-sample magnetometer''' (VSM) (also referred to as a Foner magnetometer) is a scientific instrument that measures magnetic properties based on Faraday’s Law of Induction. Simon Foner at [[MIT Lincoln Laboratory]] invented VSM in 1955 and reported it in 1959.<ref>{{cite journal|last=Foner|first=Simon|year=1959|title=Versatile and Sensitive Vibrating-Sample Magnetometer|journal=Rev. Sci. Instrum.|volume=30|issue=7|pages=548–557|bibcode=1959RScI...30..548F|doi=10.1063/1.1716679}}</ref> Also it was mentioned by G.W. Van Oosterhout<ref>{{Cite journal|last=Van Oosterhout|first=G.W.|date=1956|journal=Appl. Sci. Res.|volume=B6|pages=101}}</ref> and by P.J Flanders in 1956.<ref>{{Cite journal|last=Flanders|first=P.J.|date=1956|journal=IEEE Special Publication, Conference on Magnetism and Magnetic Materials|volume=T-91|pages=315–317}}</ref> A sample is first placed in a constant magnetic field and if the sample is magnetic it will align its magnetization with the external field. The [[Magnetic moment|magnetic dipole moment]] of the sample creates a magnetic field that changes as a function of time as the sample is moved up and down. This is typically done through the use of a [[piezoelectric]] material. The alternating magnetic field induces an electric field in the pickup coils of the VSM.<ref name=":0">{{Cite web|last=SWT Physics Department|title=Vibrating Sample Magnetometer|url=https://gato-docs.its.txstate.edu/jcr:7543b8ec-f619-49c3-888f-01c3ad13c7da/vsm.pdf|url-status=live}}</ref> The current is proportional to the magnetization of the sample - the greater the induced current, the greater the magnetization. As a result, typically a [[Hysteresis|hysteresis curve]] will be recorded<ref name=":1">{{Cite journal|last1=Lopez-Dominguez|first1=V.|last2=Quesada|first2=A.|last3=Guzmán-Mínguez|first3=J. C.|last4=Moreno|first4=L.|last5=Lere|first5=M.|last6=Spottorno|first6=J.|last7=Giacomone|first7=F.|last8=Fernández|first8=J. F.|last9=Hernando|first9=A.|last10=García|first10=M. A.|date=2018-03-01|title=A simple vibrating sample magnetometer for macroscopic samples|url=https://aip.scitation.org/doi/10.1063/1.5017708|journal=Review of Scientific Instruments|volume=89|issue=3|pages=034707|doi=10.1063/1.5017708|pmid=29604780 |bibcode=2018RScI...89c4707L |issn=0034-6748|hdl=10261/163494|hdl-access=free}}</ref> and from there we can deduce the magnetic properties of the sample being measured. |
||
The idea of vibrating sample came from D. O. Smith's<ref>{{Cite journal|last=Smith|first=D. O.|year=1956|title=Development of a Vibrating‐Coil Magnetometer|journal=Rev. Sci. Instrum.|volume=27|issue=261|pages=261–268|bibcode=1956RScI...27..261S|doi=10.1063/1.1715538}}</ref> vibrating-coil [[magnetometer]]. |
The idea of vibrating sample came from D. O. Smith's<ref>{{Cite journal|last=Smith|first=D. O.|year=1956|title=Development of a Vibrating‐Coil Magnetometer|journal=Rev. Sci. Instrum.|volume=27|issue=261|pages=261–268|bibcode=1956RScI...27..261S|doi=10.1063/1.1715538}}</ref> vibrating-coil [[magnetometer]]. |
||
Line 32: | Line 32: | ||
# Magnetic field must be strong enough to fully saturate the samples (or else inaccurate measurements will be taken) |
# Magnetic field must be strong enough to fully saturate the samples (or else inaccurate measurements will be taken) |
||
# Magnetic field must be uniform across the sample space (otherwise the addition of field gradients<ref name=":1" /><ref name=":2">{{Cite journal| |
# Magnetic field must be uniform across the sample space (otherwise the addition of field gradients<ref name=":1" /><ref name=":2">{{Cite journal|last1=Burgei|first1=Wesley|last2=Pechan|first2=Michael J.|last3=Jaeger|first3=Herbert|date=2003-07-10|title=A simple vibrating sample magnetometer for use in a materials physics course|url=https://aapt.scitation.org/doi/10.1119/1.1572149|journal=American Journal of Physics|volume=71|issue=8|pages=825–828|doi=10.1119/1.1572149|bibcode=2003AmJPh..71..825B |issn=0002-9505}}</ref> will induce force that alter the vibration once again leading to inaccurate results |
||
==== Importance of pick-up coils ==== |
==== Importance of pick-up coils ==== |
Revision as of 19:48, 10 June 2022
A vibrating-sample magnetometer (VSM) (also referred to as a Foner magnetometer) is a scientific instrument that measures magnetic properties based on Faraday’s Law of Induction. Simon Foner at MIT Lincoln Laboratory invented VSM in 1955 and reported it in 1959.[1] Also it was mentioned by G.W. Van Oosterhout[2] and by P.J Flanders in 1956.[3] A sample is first placed in a constant magnetic field and if the sample is magnetic it will align its magnetization with the external field. The magnetic dipole moment of the sample creates a magnetic field that changes as a function of time as the sample is moved up and down. This is typically done through the use of a piezoelectric material. The alternating magnetic field induces an electric field in the pickup coils of the VSM.[4] The current is proportional to the magnetization of the sample - the greater the induced current, the greater the magnetization. As a result, typically a hysteresis curve will be recorded[5] and from there we can deduce the magnetic properties of the sample being measured.
The idea of vibrating sample came from D. O. Smith's[6] vibrating-coil magnetometer.
Typical VSM overview
Parts of a typical VSM setup
- Actively cooled electromagnet/power supply
- Amplifier
- Control Chassis
- Meter
- Computer interface
- Sensor coils
- Vibration exciter with sample holder
- Hall probe (optional)
Sample Operating Procedure:[4]
- Mounting the sample in the sample holder
- Turning on the VSM system
- Run the computer software to initialize the system
- Calibrate the system
- Optimize the system for M[4]
- Calibrate the Lock-In Amplifier
- Take measurements and record data
Conditions for VSM to be effective
- Magnetic field must be strong enough to fully saturate the samples (or else inaccurate measurements will be taken)
- Magnetic field must be uniform across the sample space (otherwise the addition of field gradients[5][7] will induce force that alter the vibration once again leading to inaccurate results
Importance of pick-up coils
These allow the VSM to maximize the induced signal, reduce the noise, give a wide saddle point, minimize the volume in between the sample and electromagnet to achieve a more uniform magnetic field at the sample space.[5] The configuration of the coils can vary depending on the type of material being studied.[5]
Relation to Physics
The VSM relies on Faraday's law of induction, with the detection of the emf given by ,[7] where N is the number of wire turns, A is the area, and the angle between the normal of the coil and the B field. However, N and A are often unnecessary if the VSM is properly calibrated.[7] By varying the strength of the electromagnet through computer software, the external field is sweeped from high to low and back to high.[7] Typically this is automated through a computer process and a cycle of data is printed out. The electromagnet is typically attached to a rotating base[7] so as to allow the measurements be taken as a function of angle. The external field is applied parallel to the sample length[7] and the aforementioned cycle prints out a hysteresis loop. Then using known magnetization of the calibration material and wire volume the high field voltage signal can be converted into emu units - useful for analysis.[7]
Advantages and Disadvantages
The precision and accuracy of VSM's are quite high even among other magnetometers and can be on the order of ~ emu.[5] VSM's further allow for a sample to be tested at varying angles with respect to its magnetization letting researches minimize the effects of external influences.[8] However, VSM's are not well suited for determining the magnetization loop due to the demagnetizing effects incurred by the sample.[8] VSM's further suffer from temperature dependence and cannot be used on fragile samples that cannot undergo acceleration (from the vibration).[5][7][8]
References
- ^ Foner, Simon (1959). "Versatile and Sensitive Vibrating-Sample Magnetometer". Rev. Sci. Instrum. 30 (7): 548–557. Bibcode:1959RScI...30..548F. doi:10.1063/1.1716679.
- ^ Van Oosterhout, G.W. (1956). Appl. Sci. Res. B6: 101.
{{cite journal}}
: Missing or empty|title=
(help) - ^ Flanders, P.J. (1956). IEEE Special Publication, Conference on Magnetism and Magnetic Materials. T-91: 315–317.
{{cite journal}}
: Missing or empty|title=
(help) - ^ a b c SWT Physics Department. "Vibrating Sample Magnetometer" (PDF).
{{cite web}}
: CS1 maint: url-status (link) - ^ a b c d e f Lopez-Dominguez, V.; Quesada, A.; Guzmán-Mínguez, J. C.; Moreno, L.; Lere, M.; Spottorno, J.; Giacomone, F.; Fernández, J. F.; Hernando, A.; García, M. A. (2018-03-01). "A simple vibrating sample magnetometer for macroscopic samples". Review of Scientific Instruments. 89 (3): 034707. Bibcode:2018RScI...89c4707L. doi:10.1063/1.5017708. hdl:10261/163494. ISSN 0034-6748. PMID 29604780.
- ^ Smith, D. O. (1956). "Development of a Vibrating‐Coil Magnetometer". Rev. Sci. Instrum. 27 (261): 261–268. Bibcode:1956RScI...27..261S. doi:10.1063/1.1715538.
- ^ a b c d e f g h Burgei, Wesley; Pechan, Michael J.; Jaeger, Herbert (2003-07-10). "A simple vibrating sample magnetometer for use in a materials physics course". American Journal of Physics. 71 (8): 825–828. Bibcode:2003AmJPh..71..825B. doi:10.1119/1.1572149. ISSN 0002-9505.
- ^ a b c "Interpretation of Vibrating Sample Magnetometer (VSM) analysis". analyzetest.com. 2021-03-16. Retrieved 2021-05-14.