Young's modulus

In solid mechanics, Young's modulus (E) is a measure of the stiffness of an isotropic elastic material. It is also known as the Young modulus, modulus of elasticity, elastic modulus (though Young's modulus is actually one of several elastic moduli such as the bulk modulus and the shear modulus) or tensile modulus. It is defined as the ratio of the uniaxial stress over the uniaxial strain in the range of stress in which Hooke's Law holds. This can be experimentally determined from the slope of a stress-strain curve created during tensile tests conducted on a sample of the material.

Young's modulus is named after Thomas Young, the 19th century British scientist. However, the concept was developed in 1727 by Leonhard Euler, and the first experiments that used the concept of Young's modulus in its current form were performed by the Italian scientist Giordano Riccati in 1782 — predating Young's work by 25 years.

Units

Young's modulus is the ratio of stress, which has units of pressure, to strain, which is dimensionless; therefore Young's modulus itself has units of pressure.

The SI unit of modulus of elasticity (E, or less commonly Y) is the pascal (Pa or N/m²); the practical units are megapascals (MPa or N/mm²) or gigapascals (GPa or kN/mm²). In United States customary units, it is expressed as pounds (force) per square inch (psi).

Usage

The Young's modulus allows the behavior of a bar made of an isotropic elastic material to be calculated under tensile or compressive loads. For instance, it can be used to predict the amount a wire will extend under tension or buckle under compression. Some calculations also require the use of other material properties, such as the shear modulus, density, or Poisson's ratio.

Linear versus non-linear

For many materials, Young's modulus is essentially constant over a range of strains. Such materials are called linear, and are said to obey Hooke's law. Examples of linear materials include steel, carbon fiber, and glass. Rubber and soils (except at very small strains) are non-linear materials.

Directional materials

Young's modulus is not always the same in all orientations of a material. Most metals and ceramics, along with many other materials, are isotropic: Their mechanical properties are the same in all orientations. However, metals and ceramics can be treated with certain impurities, and metals can be mechanically worked to make their grain structures directional. These materials then become anisotropic, and Young's modulus will change depending on the direction from which the force is applied. Anisotropy can be seen in many composites as well. For example, carbon fiber has a much higher Young's modulus (is much stiffer) when force is loaded parallel to the fibers (along the grain). Other such materials include wood and reinforced concrete. Engineers can use this directional phenomenon to their advantage in creating structures.

Calculation

Young's modulus, E, can be calculated by dividing the tensile stress by the tensile strain:

$E\equiv {\frac {\mbox{tensile stress}}{\mbox{tensile strain}}}={\frac {\sigma }{\varepsilon }}={\frac {F/A_{0}}{\Delta L/L_{0}}}={\frac {FL_{0}}{A_{0}\Delta L}}$

where

E is the Young's modulus (modulus of elasticity)

F is the force applied to the object;

A₀ is the original cross-sectional area through which the force is applied;

ΔL is the amount by which the length of the object changes;

L₀ is the original length of the object.

Force exerted by stretched or compressed material

The Young's modulus of a material can be used to calculate the force it exerts under a specific strain.

$F={\frac {EA_{0}\Delta L}{L_{0}}}$

where F is the force exerted by the material when compressed or stretched by ΔL.

Hooke's law can be derived from this formula, which describes the stiffness of an ideal spring:

$F=\left({\frac {EA_{0}}{L_{0}}}\right)\Delta L=kx\,$

where

$k={\begin{matrix}{\frac {EA_{0}}{L_{0}}}\end{matrix}}\,$

$x=\Delta L.\,$

Elastic potential energy

The elastic potential energy stored is given by the integral of this expression with respect to L:

$U_{e}=\int {\frac {EA_{0}\Delta L}{L_{0}}}\,dL={\frac {EA_{0}}{L_{0}}}\int {\Delta L}\,dL={\frac {EA_{0}{\Delta L}^{2}}{2L_{0}}}$

where U_e is the elastic potential energy.

The elastic potential energy per unit volume is given by:

${\frac {U_{e}}{A_{0}L_{0}}}={\frac {E{\Delta L}^{2}}{2L_{0}^{2}}}={\frac {1}{2}}E{\varepsilon }^{2}$, where $\varepsilon ={\frac {\Delta L}{L_{0}}}$ is the strain in the material.

This formula can also be expressed as the integral of Hooke's law:

$U_{e}=\int {kx}\,dx={\frac {1}{2}}kx^{2}.$

Relation among elastic constants

For homogeneous isotropic materials simple relations exist between elastic constants (Young's modulus E, shear modulus G, bulk modulus K, and Poisson's ratio ν) that allow calculating them all as long as two are known:

$E=2G(1+\nu )=3K(1-2\nu ).\,$

Approximate values

Influences of selected glass component additions on Young's modulus of a specific base glass

Young's modulus can vary somewhat due to differences in sample composition and test method. The rate of deformation has the greatest impact on the data collected, especially in polymers. The values here are approximate and only meant for relative comparisons.

Approximate Young's modulus for various materials

Material	GPa	lbf/in² (psi)
Rubber (small strain)	0.01-0.1	1,500-15,000
ZnO NWs	21-37	3,045,792-5,366,396
PTFE (Teflon)	0.5	75,000
Low density polyethylene	0.2	30,000
HDPE	0.8
Polypropylene	1.5-2	217,000-290,000
Bacteriophage capsids	1-3	150,000-435,000
Polyethylene terephthalate	2-2.7
Polystyrene	3-3.5	435,000-505,000
Nylon	2-4	290,000-580,000
Diatom frustules (largely silicic acid)	0.35-2.77	50,000-400,000
Medium-density fibreboard	3.654	530,000
Pine wood (along grain)	8.963	1,300,000
Oak wood (along grain)	11	1,600,000
High-strength concrete (under compression)	30	4,350,000
Magnesium metal (Mg)	45	6,500,000
Aluminium	69	10,000,000
Glass (see chart)	50-90
Kevlar	70.5-112.4
Mother-of-pearl (nacre, largely calcium carbonate)	70	10,000,000
Tooth enamel (largely calcium phosphate)	83	12,000,000
Brass and bronze	100-125	17,000,000
Titanium (Ti)		16,000,000
Titanium alloys	105-120	15,000,000-17,500,000
Copper (Cu)	117	17,000,000
Glass fiber reinforced plastic (70/30 by weight fibre/matrix, unidirectional, along grain)	40-45	5,800,000-6,500,000
Carbon fiber reinforced plastic (50/50 fibre/matrix, unidirectional, along grain)	125-150	18,000,000-22,000,000
Wrought iron	190–210
Steel	200	29,000,000
polycrystalline Yttrium iron garnet (YIG)	193	28,000,000
single-crystal Yttrium iron garnet (YIG)	200	30,000,000
Beryllium (Be)	287	42,000,000
Tungsten (W)	400-410	58,000,000-59,500,000
Sapphire (Al2O3) along C-axis	435	63,000,000
Silicon carbide (SiC)	450	65,000,000
Osmium (Os)	550	79,800,000
Tungsten carbide (WC)	450-650	65,000,000-94,000,000
Single-walled carbon nanotube	1,000+	145,000,000+
Diamond (C)	1220	150,000,000-175,000,000

See also

• Deflection
• Deformation
• Hardness
• Hooke's law
• Shear modulus
• Bending stiffness
• Impulse excitation technique
• Toughness
• Yield (engineering)
• List of materials properties

External links

• Matweb: free database of engineering properties for over 63,000 materials
• Young's Modulus for groups of materials, and their cost
• Young's Modulus as function of temperature

Conversion formulae
Homogeneous isotropic linear elastic materials have their elastic properties uniquely determined by any two moduli among these; thus, given any two, any other of the elastic moduli can be calculated according to these formulas, provided both for 3D materials (first part of the table) and for 2D materials (second part).
3D formulae	$K=\,$	$E=\,$	$\lambda =\,$	$G=\,$	$\nu =\,$	$M=\,$	Notes
$(K,\,E)$			${\tfrac {3K(3K-E)}{9K-E}}$	${\tfrac {3KE}{9K-E}}$	${\tfrac {3K-E}{6K}}$	${\tfrac {3K(3K+E)}{9K-E}}$
$(K,\,\lambda )$		${\tfrac {9K(K-\lambda )}{3K-\lambda }}$		${\tfrac {3(K-\lambda )}{2}}$	${\tfrac {\lambda }{3K-\lambda }}$	$3K-2\lambda \,$
$(K,\,G)$		${\tfrac {9KG}{3K+G}}$	$K-{\tfrac {2G}{3}}$		${\tfrac {3K-2G}{2(3K+G)}}$	$K+{\tfrac {4G}{3}}$
$(K,\,\nu )$		$3K(1-2\nu )\,$	${\tfrac {3K\nu }{1+\nu }}$	${\tfrac {3K(1-2\nu )}{2(1+\nu )}}$		${\tfrac {3K(1-\nu )}{1+\nu }}$
$(K,\,M)$		${\tfrac {9K(M-K)}{3K+M}}$	${\tfrac {3K-M}{2}}$	${\tfrac {3(M-K)}{4}}$	${\tfrac {3K-M}{3K+M}}$
$(E,\,\lambda )$	${\tfrac {E+3\lambda +R}{6}}$			${\tfrac {E-3\lambda +R}{4}}$	${\tfrac {2\lambda }{E+\lambda +R}}$	${\tfrac {E-\lambda +R}{2}}$	$R={\sqrt {E^{2}+9\lambda ^{2}+2E\lambda }}$
$(E,\,G)$	${\tfrac {EG}{3(3G-E)}}$		${\tfrac {G(E-2G)}{3G-E}}$		${\tfrac {E}{2G}}-1$	${\tfrac {G(4G-E)}{3G-E}}$
$(E,\,\nu )$	${\tfrac {E}{3(1-2\nu )}}$		${\tfrac {E\nu }{(1+\nu )(1-2\nu )}}$	${\tfrac {E}{2(1+\nu )}}$		${\tfrac {E(1-\nu )}{(1+\nu )(1-2\nu )}}$
$(E,\,M)$	${\tfrac {3M-E+S}{6}}$		${\tfrac {M-E+S}{4}}$	${\tfrac {3M+E-S}{8}}$	${\tfrac {E-M+S}{4M}}$		$S=\pm {\sqrt {E^{2}+9M^{2}-10EM}}$ There are two valid solutions. The plus sign leads to $\nu \geq 0$. The minus sign leads to $\nu \leq 0$.
$(\lambda ,\,G)$	$\lambda +{\tfrac {2G}{3}}$	${\tfrac {G(3\lambda +2G)}{\lambda +G}}$			${\tfrac {\lambda }{2(\lambda +G)}}$	$\lambda +2G\,$
$(\lambda ,\,\nu )$	${\tfrac {\lambda (1+\nu )}{3\nu }}$	${\tfrac {\lambda (1+\nu )(1-2\nu )}{\nu }}$		${\tfrac {\lambda (1-2\nu )}{2\nu }}$		${\tfrac {\lambda (1-\nu )}{\nu }}$	Cannot be used when $\nu =0\Leftrightarrow \lambda =0$
$(\lambda ,\,M)$	${\tfrac {M+2\lambda }{3}}$	${\tfrac {(M-\lambda )(M+2\lambda )}{M+\lambda }}$		${\tfrac {M-\lambda }{2}}$	${\tfrac {\lambda }{M+\lambda }}$
$(G,\,\nu )$	${\tfrac {2G(1+\nu )}{3(1-2\nu )}}$	$2G(1+\nu )\,$	${\tfrac {2G\nu }{1-2\nu }}$			${\tfrac {2G(1-\nu )}{1-2\nu }}$
$(G,\,M)$	$M-{\tfrac {4G}{3}}$	${\tfrac {G(3M-4G)}{M-G}}$	$M-2G\,$		${\tfrac {M-2G}{2M-2G}}$
$(\nu ,\,M)$	${\tfrac {M(1+\nu )}{3(1-\nu )}}$	${\tfrac {M(1+\nu )(1-2\nu )}{1-\nu }}$	${\tfrac {M\nu }{1-\nu }}$	${\tfrac {M(1-2\nu )}{2(1-\nu )}}$
2D formulae	$K_{\mathrm {2D} }=\,$	$E_{\mathrm {2D} }=\,$	$\lambda _{\mathrm {2D} }=\,$	$G_{\mathrm {2D} }=\,$	$\nu _{\mathrm {2D} }=\,$	$M_{\mathrm {2D} }=\,$	Notes
$(K_{\mathrm {2D} },\,E_{\mathrm {2D} })$			${\tfrac {2K_{\mathrm {2D} }(2K_{\mathrm {2D} }-E_{\mathrm {2D} })}{4K_{\mathrm {2D} }-E_{\mathrm {2D} }}}$	${\tfrac {K_{\mathrm {2D} }E_{\mathrm {2D} }}{4K_{\mathrm {2D} }-E_{\mathrm {2D} }}}$	${\tfrac {2K_{\mathrm {2D} }-E_{\mathrm {2D} }}{2K_{\mathrm {2D} }}}$	${\tfrac {4K_{\mathrm {2D} }^{2}}{4K_{\mathrm {2D} }-E_{\mathrm {2D} }}}$
$(K_{\mathrm {2D} },\,\lambda _{\mathrm {2D} })$		${\tfrac {4K_{\mathrm {2D} }(K_{\mathrm {2D} }-\lambda _{\mathrm {2D} })}{2K_{\mathrm {2D} }-\lambda _{\mathrm {2D} }}}$		$K_{\mathrm {2D} }-\lambda _{\mathrm {2D} }$	${\tfrac {\lambda _{\mathrm {2D} }}{2K_{\mathrm {2D} }-\lambda _{\mathrm {2D} }}}$	$2K_{\mathrm {2D} }-\lambda _{\mathrm {2D} }$
$(K_{\mathrm {2D} },\,G_{\mathrm {2D} })$		${\tfrac {4K_{\mathrm {2D} }G_{\mathrm {2D} }}{K_{\mathrm {2D} }+G_{\mathrm {2D} }}}$	$K_{\mathrm {2D} }-G_{\mathrm {2D} }$		${\tfrac {K_{\mathrm {2D} }-G_{\mathrm {2D} }}{K_{\mathrm {2D} }+G_{\mathrm {2D} }}}$	$K_{\mathrm {2D} }+G_{\mathrm {2D} }$
$(K_{\mathrm {2D} },\,\nu _{\mathrm {2D} })$		$2K_{\mathrm {2D} }(1-\nu _{\mathrm {2D} })\,$	${\tfrac {2K_{\mathrm {2D} }\nu _{\mathrm {2D} }}{1+\nu _{\mathrm {2D} }}}$	${\tfrac {K_{\mathrm {2D} }(1-\nu _{\mathrm {2D} })}{1+\nu _{\mathrm {2D} }}}$		${\tfrac {2K_{\mathrm {2D} }}{1+\nu _{\mathrm {2D} }}}$
$(E_{\mathrm {2D} },\,G_{\mathrm {2D} })$	${\tfrac {E_{\mathrm {2D} }G_{\mathrm {2D} }}{4G_{\mathrm {2D} }-E_{\mathrm {2D} }}}$		${\tfrac {2G_{\mathrm {2D} }(E_{\mathrm {2D} }-2G_{\mathrm {2D} })}{4G_{\mathrm {2D} }-E_{\mathrm {2D} }}}$		${\tfrac {E_{\mathrm {2D} }}{2G_{\mathrm {2D} }}}-1$	${\tfrac {4G_{\mathrm {2D} }^{2}}{4G_{\mathrm {2D} }-E_{\mathrm {2D} }}}$
$(E_{\mathrm {2D} },\,\nu _{\mathrm {2D} })$	${\tfrac {E_{\mathrm {2D} }}{2(1-\nu _{\mathrm {2D} })}}$		${\tfrac {E_{\mathrm {2D} }\nu _{\mathrm {2D} }}{(1+\nu _{\mathrm {2D} })(1-\nu _{\mathrm {2D} })}}$	${\tfrac {E_{\mathrm {2D} }}{2(1+\nu _{\mathrm {2D} })}}$		${\tfrac {E_{\mathrm {2D} }}{(1+\nu _{\mathrm {2D} })(1-\nu _{\mathrm {2D} })}}$
$(\lambda _{\mathrm {2D} },\,G_{\mathrm {2D} })$	$\lambda _{\mathrm {2D} }+G_{\mathrm {2D} }$	${\tfrac {4G_{\mathrm {2D} }(\lambda _{\mathrm {2D} }+G_{\mathrm {2D} })}{\lambda _{\mathrm {2D} }+2G_{\mathrm {2D} }}}$			${\tfrac {\lambda _{\mathrm {2D} }}{\lambda _{\mathrm {2D} }+2G_{\mathrm {2D} }}}$	$\lambda _{\mathrm {2D} }+2G_{\mathrm {2D} }\,$
$(\lambda _{\mathrm {2D} },\,\nu _{\mathrm {2D} })$	${\tfrac {\lambda _{\mathrm {2D} }(1+\nu _{\mathrm {2D} })}{2\nu _{\mathrm {2D} }}}$	${\tfrac {\lambda _{\mathrm {2D} }(1+\nu _{\mathrm {2D} })(1-\nu _{\mathrm {2D} })}{\nu _{\mathrm {2D} }}}$		${\tfrac {\lambda _{\mathrm {2D} }(1-\nu _{\mathrm {2D} })}{2\nu _{\mathrm {2D} }}}$		${\tfrac {\lambda _{\mathrm {2D} }}{\nu _{\mathrm {2D} }}}$	Cannot be used when $\nu _{\mathrm {2D} }=0\Leftrightarrow \lambda _{\mathrm {2D} }=0$
$(G_{\mathrm {2D} },\,\nu _{\mathrm {2D} })$	${\tfrac {G_{\mathrm {2D} }(1+\nu _{\mathrm {2D} })}{1-\nu _{\mathrm {2D} }}}$	$2G_{\mathrm {2D} }(1+\nu _{\mathrm {2D} })\,$	${\tfrac {2G_{\mathrm {2D} }\nu _{\mathrm {2D} }}{1-\nu _{\mathrm {2D} }}}$			${\tfrac {2G_{\mathrm {2D} }}{1-\nu _{\mathrm {2D} }}}$
$(G_{\mathrm {2D} },\,M_{\mathrm {2D} })$	$M_{\mathrm {2D} }-G_{\mathrm {2D} }$	${\tfrac {4G_{\mathrm {2D} }(M_{\mathrm {2D} }-G_{\mathrm {2D} })}{M_{\mathrm {2D} }}}$	$M_{\mathrm {2D} }-2G_{\mathrm {2D} }\,$		${\tfrac {M_{\mathrm {2D} }-2G_{\mathrm {2D} }}{M_{\mathrm {2D} }}}$